Additives and functional resins for coatings and inks
New energy, semiconductor additives
Model number
JIAZHI®JZ-9510
Specification
|
Composition |
Silicon modified hydroxyl acrylic resin solution |
|
Appearance |
Slight yellowish to yellowish liquid |
|
Solvent |
BAC/ PMA |
|
Content |
50±3%(140℃ 2h) |
|
Density |
0.99-1.03g/ml(25±1)℃ |
|
Viscosity |
1000-6000mPa·s |
|
Hydroxyl value |
120±5 mg KOH/g (Theoretical value of solid resin) |
Note: This datasheet is intended to give typical results, not standard.Subject to COA.
Application system
Solvent-based
Properties
Increase slip. Improve hydrophobicity and oleophobicity.
Provide anti-marker wiping performance.
Provide lotus.
Excellent compatibility.
Compared with anti-graffiti additive, better anti-graffiti effect and solvent-resistant wiping performance.
Water contact angle ＞100°
Storage stability
Store in a cool, dry place in the unopened original packaging for 36 months. Products that exceed the storage period can continue to be used after passing the inspection. It must be closed immediately after use.
Recommended formula
|
1. Suggestion for PU varnish formulation |
|||
|
|
Material |
Dosage% |
|
|
Part A |
JZ-9510 |
76.0 |
|
|
PMA |
22.65-22.74 |
||
|
Dryer(1%) |
1.0 |
||
|
WE-D8920BR(leveling agent) |
0.25 |
||
|
WE-D980(defoamer) |
0.01-0.1 |
||
|
Total |
100 |
||
|
Part B |
N3390 |
18 |
|
Note： 1.Usage recommendation for defoamerAdd WE-D980 with 0.01% to PU varnish and no affecting of compatibility. Can increase the addition to 0.1% of WE-D980 to color paint.
2.NCO% of N3390=19.6, produced by Covestro, Germany.
3.The mixed part A and B should be used up within 5-7 hours in a sealed container. Otherwise, the mixed material will be gelled.
4.Suggest dry it at 80℃ for 1h or 150℃ for 5min.
2. Suggestion for baking formulation
|
Product name |
Dosage% |
||
|
JZ-9510 |
50 |
||
|
Butylenized amino resin |
10 |
||
|
Solvent |
38.5 |
||
|
Adhesion promoter |
1 |
||
|
Acid catalyst |
0.5 |
||
|
Ttotal |
100 |
Note：Amino resin in this formulation is Sanmu582, and its addition should be adjusted to specific requirements. Suggest dry it at 150℃ for 30min or 210℃ for 90s.
Package
25KG / 180KG
Go